Scientists at the University of California find a fluid solution to dendrite growth in lithium metal batteries

Dendrite growth reduced 99 percent


KEY POINTS
  • Lithium metal batteries have a higher charge density than conventional lithium-ion batteries but are prone to problems of tree-like metal dendrites, which can cause short circuits or explosions.
  • A new article shows that flowing ions near the cathode can prevent this problem.

A new paper from associate professor Jiandi Wan’s group in the UC Davis Department of Chemical Engineering, published in Science Advances, proposes a potential solution to dendrite growth in rechargeable lithium metal batteries.



In the paper, Wan’s team proves that flowing ions near the cathode can potentially expand the safety and lifespans of these next-generation rechargeable batteries.

Lithium metal batteries use lithium metal as the anode. These batteries have a high charge density and potentially double the energy of conventional lithium-ion batteries, but safety is a big concern. When they charge, some ions are reduced to lithium metal at the cathode surface and form irregular, tree-like microstructures known as dendrites, which can eventually cause a short circuit or even an explosion.

The theory is that dendrite growth is caused by the competition of mass transfer and reduction rate of lithium ions near the cathode surface. When the reduction rate of ions is much faster than the mass transfer, it creates an electroneutral gap called the space-charged layer near the cathode that contains no ions. The instability of this layer is thought to cause dendrite growth, so reducing or eliminating it might reduce dendrite growth and therefore extend the life of a battery.

Dendrite growth reduced 99 percent

Wan’s idea was to flow ions through the cathode in a microfluidic channel to restore a charge and offset this gap. In the paper, the team outlined their proof-of-concept tests, finding that this flow of ions could reduce dendrite growth by up to 99 percent.

For Wan, the study is exciting because it shows the effectiveness of applying microfluidics to battery-related problems and paves the way for future research in this area.

“With this fundamental study and microfluidic approaches, we were able to quantitatively understand the effect of flow on dendrite growth,” he said. “Not many groups have studied this yet.”

Though it is likely not possible to directly incorporate microfluidics in real batteries, Wan’s group is looking at alternative ways to apply the fundamental principles from this study and introduce local flows near the cathode surface to compensate cations and eliminate the space charge layer.

“We are quite excited to explore the new applications of our study,” he said. “We are already working on design of the cathode surface to introduce convective flows.”

—-
Publication Referenced in the Article:

Meghann C. Ma, Gaojin Li, Xinye Chen, Lynden A. Archer, Jiandi Wan. Suppression of dendrite growth by cross-flow in microfluidics. Science Advances, 2021; 7 (8): eabf6941 DOI: 10.1126/sciadv.abf6941

More Stories on this Topic

More Stories From Around the Web:

Leave a Reply